Optical Window BK7 30mm Diameter Anti-reflection Coated 633 - 1064nm
WBMA-30C02-10-IR1
These optical windows have high-quality and may be used when light is passed through the opposite side of the partition or in the vacuum chamber. Since the windows have anti-reflection coatings the transmittance is increased so they can be used as a window for laser irradiation windows and the observation of the sample.
◦By anti-reflection coating with a dielectric multi-layer, it is reduced to less than 1% to 4% reflection loss of the glass surface.
◦Since we are using the high quality material, the image will not be distorted by the transmission of the glass, and the laser beam is not diffused.
◦When you insert an window perpendicular to the optical path of the laser, the angle of the transmitted beam will not be changed.
◦Since we are using the high quality material, the image will not be distorted by the transmission of the glass, and the laser beam is not diffused.
◦When you insert an window perpendicular to the optical path of the laser, the angle of the transmitted beam will not be changed.
| Name | Optical Window BK7 30mm Diameter Anti-reflection Coated 633 - 1064nm |
|---|---|
| Weight | 0.0050kgs |
| Standard Coatings Available | No |
| Guide |
|
| Remark | - |
| Attention |
|
| Diameter φD | 30mm |
| Image Label | Optical Window BK7 30mm Diameter Anti-reflection Coated 633 - 1064nm |
| Material | BK7 |
| Surface flatness | λ/10 |
| Parallelism | ＜5″ |
| Coating | Dielectric multi-layer coating |
| Incident angle | 0° |
| Laser Damage Threshold | 4J/cm2 |
| Surface Quality <br> (Scratch-Dig) | 40-20 |
| Wavelength range | 633 - 1064nm |
| Diameter φD | φ30mm |
| Thickness t | 2mm |
In stock
SKU
WBMA-30C02-10-IR1
$118.00
Customize product
These optical windows have high-quality and may be used when light is passed through the opposite side of the partition or in the vacuum chamber. Since the windows have anti-reflection coatings the transmittance is increased so they can be used as a window for laser irradiation windows and the observation of the sample.