UV Enhanced Aluminum Round Flat Mirrors

TFAE-C

UV Enhanced Aluminum Round Flat Mirrors
In stock
SKU
TFAE-C
This is a vapor-deposited aluminum flat mirror with the substrate polished with high accuracy, designed for high reflectivity at any incident angle.
custom product
Customize product
Filters
Enabled filters :
Remove all filters
Name Diameter φD Material Rear Surface Reflectance Delivery Price Add to cart
i
Enhanced Aluminum Mirror 25.4mm Diameter Wavelength Range 170 - 400nm
TFAE-25.4C05-10
25.4mm BK7 Polished Rave.>85%
3-5 days
£91.50
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 170 - 400nm
Reflectance Rave.>85%
Diameter φD φ25.4mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Polished
i
Enhanced Aluminum Mirror 12.7mm Diameter Wavelength Range 400 - 700nm
TFAE-12.7C05-10-550
12.7mm BK7 Ground Rave.>94%
3-5 days
£73.20
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 400 - 700nm
Reflectance Rave.>94%
Diameter φD φ12.7mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Ground
i
Enhanced Aluminum Mirror 30mm Diameter Wavelength Range 170 - 400nm
TFAE-30C05-10
30mm BK7 Polished Rave.>85%
6-12 weeks
£109.80
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 170 - 400nm
Reflectance Rave.>85%
Diameter φD φ30mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Polished
i
Enhanced Aluminum Mirror 25.4mm Diameter Wavelength Range 400 - 700nm
TFAE-25.4C05-10-550
25.4mm BK7 Polished Rave.>94%
6-12 weeks
£82.30
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 400 - 700nm
Reflectance Rave.>94%
Diameter φD φ25.4mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Polished
i
Enhanced Aluminum Mirror 12.7mm Diameter Wavelength Range 170 - 400nm
TFAE-12.7C05-10
12.7mm BK7 Ground Rave.>85%
3-5 days
£78.70
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 170 - 400nm
Reflectance Rave.>85%
Diameter φD φ12.7mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Ground
i
Enhanced Aluminum Mirror 50mm Diameter Wavelength Range 170 - 400nm
TFAE-50C08-10
50mm BK7 Polished Rave.>85%
3-5 days
£192.10
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 170 - 400nm
Reflectance Rave.>85%
Diameter φD φ50mm
Thickness t 8mm
Surface Flatness λ/10
Rear surface Polished
i
Enhanced Aluminum Mirror 30mm Diameter Wavelength Range 400 - 700nm
TFAE-30C05-10-550
30mm BK7 Polished Rave.>94%
3-5 days
£82.30
Material BK7
Coating Aluminum+Dielectric multilayer coating
Parallelism <3′
Incident angle 45°
Laser Damage Threshold 0.25J/cm2
Surface Quality (Scratch-Dig) 40-20
Wavelength Range 400 - 700nm
Reflectance Rave.>94%
Diameter φD φ30mm
Thickness t 5mm
Surface Flatness λ/10
Rear surface Polished

You must be logged in to ask questions

◦With four types to choose from; (TFAN/TFAQN) which is coated with aluminum only, (TFA/TFAQ) which is coated with a protective coating against accidental hard scratches, (TFAE) which is coated aluminum and a protective coating to increase the reflectance of ultraviolet and lastly, (OPBA/OPSQA) which provides Aluminum with protective coat on the optical parallel substrate.
◦For ultraviolet, visible and near-infrared light applications.
◦For low thermal expansion mirrors, we have (TFAQ/TFAQN) which is made of Synthetic fused silica that provides high rigidity and high precision surface quality.